Related Products
ZRC
ZRC PAINT 1.5 LBS / 250 ML
95% zinc in the dry film using only Type III “ultra pure” ASTM-D-520 zinc
Technical Data
| TYPE | Single pack, premixed, ready to apply,
liquid organic zinc compound |
| THEORETICAL COVERAGE | 400 ft²/gal @ 1.5 mil dry film thickness |
| METALLIC ZINC CONTENT | 95% by weight in dry film |
| FLASH POINT | 111°F (44°C) (SETA method, ASTM D3278) |
| VOC CONTENT | 3.3 lbs/gal (385 gms/ltr) (ASTM D3960) |
| WEIGHT PER GALLON | 24 lbs. (ASTM D1475) |
| SOLIDS CONTENT | 86% (by weight)/52% (by volume) |
| VISCOSITY | 1900 cps. Brookfield spindle #5 @ 100 RPM, @ 25°C |
| MAXIMUM SERVICE TEMP - Intermittent | 750°F (399)°C |
| MAXIMUM SERVICE TEMP - Constant | 350°F (177)°C |
| ELECTRICAL CONDUCTIVITY | 73 million ohms per square @ 3 mils dry (resistivity) |
| IMPACT RESISTANCE | Greater than 30 inch-lbs. (extrusion) per ASTM-D2794 |
| ABRASION RESISTANCE | 11.5 liters per dry mil (tested @ 3 dry mils) per ASTM-D98-51 |
| POT LIFE | At least 24 hrs |
| PACKAGING | 3.5 gallon pails, gallon, quart, half-pint and aerosol cans |
| DRY TIME | Set to touch. When ambient air dried, 20-30 min.
@ 1.5 mil (38μ) thickness |
| RECOAT TIME | (Second Coat) 12 hrs. |
| TOPCOATING | After 24-48 hrs., topcoat with acrylic, epoxy, urethane or vinyl
type products. DO NOT USE alkyd, alkyd-modified acrylic, or
lacquer type products. Consult our
Guide to Topcoating for detailed instructions. |
• 95% zinc in the dry film using only Type III “ultra pure” ASTM-D-520 zinc
• Meets and exceeds Fed. Spec. DOD-P-21035A (Galvanizing Repair Spec);MIL-P-26915A (USAF Zinc Dust Primer); ASTM Des. A-780 (Standard) Practice for Repair of Damaged Hot-Dip Galvanized Coatings; SSPC-Paint20 (Specification for Zinc-Rich Primer)
• Passes 3,000 hours salt spray testing without failure (ASTM Des. B117)
• Passes Preece Test (ASTM Des. A239) for hot-dip galvanizing
• Passes 9-year subtropical testing
• Low VOC approved in all 50 states
• ISO 9001 registration assures the highest quality consistently